What is the difference between 6061 and 6061-T6 aluminum?

6061 aluminum has a lower melting temperature, lower thermal conductivity, and lower heat capacity. AL 6061-T6 has a higher yield strength and fatigue strength when compared to AL-T6 6063.

Is 6061 T651 extruded?

6061-T6 bars are produced in Round, Flat, Square, and Hex shapes. Nearly all of our 6061 bars are stocked as 6061-T6511, which are “extruded.” 6061-T6511 bars are produced to meet ASTM standards, but also meet AMS specification AMS-QQ-A-200/8.

Is 6061 t651 extruded?

Is 6061 aluminum heat-treated?

Aluminium / Aluminum 6061 alloy is heat-treated at 533°C (990°F) for a sufficient period of time followed by quenching in water. The precipitation hardening process can be performed at 160°C (320°F) for 18 h followed by air cooling.

Can 6061 aluminum be heat-treated?

6061 aluminum is known for its ductility and versatility. This alloy primarily consists of aluminum, magnesium and silicon, and it can be heated and liquid quenched to render it stronger and more durable. Heat treating 6061 aluminum makes the part physically stronger and helps keep its shape after forming.

What are the characteristics of 6061 T6511 aluminum alloy?

Although the strength of 6061 t6511 aluminum aluminum alloy cannot be compared with 2xxx series or 7xxx series, 6061-T651 aluminum alloy has many characteristics of magnesium and silicon alloys, which have good processing properties, excellent welding characteristics and electroplating properties, and good corrosion resistance.

What is the tensile strength of aluminum 6061?

Aluminum 6061 Typical Mechanical Properties at Different Temperatures. Alloy and temper. Temperature, °C (°F) Ultimate tensile strength, MPa (ksi) 0.2% offset yield strength. Elongation in 50 mm (2 in.), %, AL 6061-T6, 6061-T651. -195 (-320)

Is 6061-T6 an acceptable temperature for manufacturing?

Manufacturing job shops typically interpret a material specification of “ALUMINUM 6061-T6” as allowing 6061-T6, -T651 or -T6511. All of these are acceptable tempers, and are permitted for most applications. But, from years of experience, this is not necessarily the best interpretation.

What is Al 6061 T6?

Al-6061 aluminum alloy is a general purpose structural alloy developed by Alcoa in 1935. The temper designations mainly have 6061-T4, T451, Al 6061-T6, 6061-T651, etc.