What is 13-8 stainless steel?

ATI 13-8™ alloy (UNS S13800) is a martensitic precipitation-hardening stainless steel that has excellent strength, high hardness, superior toughness, and good corrosion resistance. Good transverse toughness properties are achieved by tight chemical composition control, low carbon content, and vacuum melting.

What does ph stand for in stainless steel?

PH stainless steels are a group of alloys that are resistant to the effects of corrosion. To increase their yield strength, these alloys are subjected to heat treatment during precipitation hardening (PH) or age hardening. You must be wondering what all these terminologies mean.

What is 13 8mo?

13-8 Mo is an age-hardening stainless steel with high strength and hardness along with good levels of resistance to both general corrosion and stress-corrosion cracking. PH 13-8 Mo has been used for aircraft components, nuclear reactor components, valve parts, fittings, landing gear parts, and pins.

What is 15 5ph stainless steel?

15-5 is a variant of the older 17-4 chromium-nickel-copper precipitation hardening stainless steel. Both alloys exhibit high strength and moderate corrosion resistance. High strength is maintained to approximately 600 degrees F.

What is 13 8 as a fraction?

1 5/8
Answer: 13/8 in a mixed fraction is 1 5/8.

What is H1000 condition?

The condition H1000 has higher aging temperature, which has as a consequence higher recovery of dislocations in a martensitic structure, coarsened Ni3Ti phase and smaller fraction of chi phase.

What is 13 over 8 as a mixed number?

What is 13 8 as a percent?

162.5%
Our percent fraction is 162.5/100, which means that 138 as a percentage is 162.5%.

What is the heat capacity of Armco pH 13-8 Mo stainless steel?

ARMCO PH 13-8 Mo Stainless Steel Condition H 1000 50.8 x 152.4 mm. (2 x 6 in.) Transverse UTS – 1496 MPa (217.0 ksi) 0.2% YS – 1365 MPa (198.0 ksi) Elong., % in 50.8 mm (2 in.) – 13.0 Red. of Area % 53.7 Data represent one test from one heat Failure Note: Identical test to Figure 30, performed on a different heat. ARMCO PH 13-8 Mo

What is 13-8 PH steel good for?

Good transverse toughness properties are achieved by tight chemical composition control, low carbon content, and vacuum melting. 13-8 PH steel provides a wide range of properties through a single precipitation hardening heat treatment. It is weldable; inert gas shielding with Helium is preferred.

What is the corrosion resistance of pH 13-8 Mo stainless?

In condition H 950, PH 13-8 Mo stainless has rusting resistance similar to that of Type 304 Stainless in 5 weight percent salt fog. In strongly oxidizing and reducing acids and in atmospheric exposures, the general-corrosion resistance of PH 13-8 Mo stainless approaches that of Type 304.

What is the microstructure of WPH 13-8 Mo weld metal?

The microstructure of WPH 13-8 Mo weld metal at room temperature consists of a small amount of delta ferrite in a martensite matrix. Presence of delta ferrite in WPH 13-8 Mo weld metal is helpful in maintaining high immunity to hot cracking.